The present study investigates the manufacturing and characterization of poly(lactic acid) (PLA)-based composites with raw and treated Poaceae, with loadings of 5, 10, and 20% wt. Before composite fabrication, the lignocellulosic fillers were analyzed using Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and microscopy to assess their chemical composition, thermal stability, and morphological features. Composites were prepared by melting PLA in a molten state with fillers, followed by injection molding. Comprehensive characterization of the obtained composites included microscopic analysis, melt flow index (MFI) testing, and differential scanning calorimetry (DSC), as well as mechanical tests (tensile and bending tests, impact test). The addition of Poaceae fibers to the PLA matrix significantly affected the mechanical and rheological properties of the composites. Incorporating 5% of cooked or alkalized fibers increased the flexural strength by 57% and 54%, respectively, compared to neat PLA. The modulus of elasticity for the composite with 20% alkalized fibers increased by as much as 35%. The fibers acted as nucleating agents, reducing the cold crystallization temperature (Tcc) by up to 15.6 °C, while alkaline residues contributed to an increased melt flow index (MFI). The conducted research provides a valuable basis and insights into the design of sustainable bio-based composites.
Kubiak et al. (Sat,) studied this question.