Non‐ionic Perylene‐Diimide Polymer as Universal Cathode Interlayer for Conventional, Inverted, and Blade‐Coated Organic Solar Cells

Abstract As a class of predominantly used cathode interlayers (CILs) in organic solar cells (OSCs), perylene‐diimide (PDI)‐based polymers exhibit intriguing characteristics of excellent charge transporting capacity and suitable energy levels. Despite that, PDI‐based CILs with satisfied film‐forming ability and adequate solvent resistance are rather rare, which not only limits the further advance of OSC performances but also hinders the practical use of PDI CILs. Herein, we designed and synthesized two non‐conjugated PDI polymers for achieving high power conversion efficiency (PCE) in diverse types of OSCs. The utilization of oligo (ethylene glycol) (OEG) linkage enhanced the n‐doping effect of PDI polymers, leading to an improved ability of the CIL to reduce work function and improve electron transporting capability. Moreover, the introduction of the non‐ionic OEG chain effectively improve the wetting property and solvent resistance of PDI polymers, so the PPDINN CIL can withstand diverse processing conditions in fabricating different OSCs, including conventional, inverted and blade‐coated devices. The binary OSC with conventional structure using PPDINN CIL showed a PCE of 18.6 %, along with an improved device stability. Besides, PPDINN is compatible with the large‐area blade‐coating technique, and a PCE of 16.6 % was achieved in the 1‐cm 2 OSC where a blade‐coated PPDINN was used.