Biogenically Synthesized ZnO and Cu-Doped ZnO Nanoparticles: Effect of Cu-Dopent Concentration and Annealing on Morphology and Optical Properties

In this work, ZnO nanoparticles and Cu-doped ZnO nanoparticles were biogenically synthesized using precipitation method in iCissus quadrangularis/i plant extract medium. The influence of Cu dopant on the crystalline structure, optical properties, and morphology of ZnO was investigated. The samples were characterized by XRD, FTIR, UV–vis spectroscopy and SEM. XRD patterns confirmed the wurtzite formation of doped and undoped ZnO nanoparticles. The average crystallite size of the neat and Cu-doped samples was ~18 nm irrespective of the amount of dopant. The annealing process enhanced the size of both the neat and Cu-doped samples. However, the influence on the size is less prominent in the Cu-doped sample than in the neat sample. The UV-visible spectral analysis shows that all the synthesized doped and undoped nano zinc oxides absorb at ~400nm. The band gap energy of Cu-doped ZnO particles was greater for unannealed samples whereas it was appreciably lowered on annealing for Cu-doped samples. SEM analysis shows rod-like morphology for the unannealed and annealed undoped zinc oxides. It is changed to flower-like morphology with the addition of 5mM Cusup2+/sup and then to nano sheet-like structure with the incorporation of higher amount of Cusup2+/sup ions. Annealing of zinc oxide samples leads to the smoothening of the surfaces with a change in morphology for the ZnO nanoparticles.