Flax–Reinforced Vitrimer Epoxy Composites Produced via RTM

Composite laminates were produced by RTM using similar glass and flax fabrics and both vitrimer epoxy and aerospace-grade epoxy, both formulated for liquid molding. Tensile and flexural properties were measured and compared, revealing that the vitrimer composites exhibited equivalent performance in flexural strength and tensile modulus, but slightly lower performance in tensile strength relative to reference epoxy composites. In general, glass–fiber composites outperformed flax–fiber composites in tension. However, both glass and flax–fiber composites yielded roughly equivalent flexural strength and tensile modulus-to-weight ratios. Flax fabrics were recovered from composites by matrix dissolution, and a second-life laminate showed full retention of the mechanical properties relative to those produced from fresh flax. Finally, a demonstration of re-forming was undertaken, showing that simple press-forming can be used to modify the composite shape. However, re-forming to a flat configuration resulted in local fiber damage and a decrease in mechanical properties. An alternative forming method was demonstrated that resulted in less fiber damage, indicating that further refinements might lead to a viable forming and re-forming process.