This study reviews the application of wire arc additive manufacturing (WAAM) technology in maritime engineering and investigates an experimentally driven analytical approach for prediction of thermal distributions based on the Rosenthal solution. Two ER70S-6 low-carbon steel WAAM cylinders were fabricated using gas metal arc welding (GMAW) and plasma arc welding (PAW) processes, with interlayer temperatures of 453 °C and 250 °C, respectively. Accurately measuring the temperature field to tailor the microstructure has long been a challenge. The results indicated a significant deviation between the analytical predictions and the experimental data. To address this discrepancy, a hybrid approach combining analytical and experimental results was implemented. Time intervals between layers, extracted from the experimental data, were incorporated into the Rosenthal equation to improve the accuracy of temperature field predictions. The microstructure at the bottom, middle, and top regions of the WAAM components was examined using optical microscopy. Tensile testing and Vickers microhardness measurements were conducted to evaluate mechanical properties. Scanning electron microscopy (SEM) was used to analyze fracture surfaces and identify fracture modes. The results were consistent with those reported for other ER70S-6 cylindrical WAAM components. This work highlights limitations of the Rosenthal solution and emphasizes the need for thermal models in WAAM applications.
Lampros et al. (Thu,) studied this question.