Co2O3 functionalized SiC membrane for dye removal: Sintering necks enable dual-functionality in low-temperature sintering and catalytic ozonation | Synapse
March 3, 2026
Co2O3 functionalized SiC membrane for dye removal: Sintering necks enable dual-functionality in low-temperature sintering and catalytic ozonation
Key Points
The Co2O3 functionalized SiC membrane significantly enhances dye removal efficiency compared to traditional methods.
Key evidence shows a substantial reduction in dye concentration by up to 80% during experimental trials.
Analysis of sintering necks highlights their role in maintaining structural integrity during low-temperature sintering.
This dual-functionality may enable expanded applications for water treatment technologies, warranting further exploration.