This study addresses the challenge of through-hole defects in ZM6 cast magnesium alloy components by proposing an innovative repair strategy using ultrasonic-assisted Tungsten Inert Gas (U-TIG) welding. The microstructure and mechanical properties of the repaired joint were systematically characterized through optical microscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD), and room-temperature tensile testing. The results indicate that, assisted by the ultrasonic energy field, the repair zone successfully reconstitutes a typical and optimized triple-phase microstructure: (1) the matrix: α-Mg solid solution (dark gray), supersaturated with Nd and Zr; (2) the strengthening phase: a eutectic Mg12Nd phase (light gray), rich in Nd, distributed along grain boundaries acting as the primary strengthening component; (3) the grain refiner: dispersed Zr-rich particles (bright white spots), which effectively pin grain boundaries. Crucially, the application of ultrasound significantly refined the α-Mg grains and transformed the continuous network of the Mg12Nd phase into a more fragmented and uniform dispersion. This refined microstructure synergistically integrates the strengthening mechanisms of solid solution, precipitation hardening, and grain refinement. Consequently, the repaired joint exhibits excellent mechanical properties, achieving over 90% of the base metal’s tensile strength and elongation at room temperature. This work not only validates the feasibility of U-TIG welding for repairing ZM6 alloys but also provides a solid theoretical foundation and a promising technical pathway for the in-service repair and remanufacturing of high-performance magnesium alloy components.
Shen et al. (Mon,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: