The effects of different finishing rolling temperatures on the microstructure and mechanical properties of a 580HE hole expansion steel were systematically investigated using optical microscopy, scanning electron microscopy, electron backscatter diffraction, and transmission electron microscopy. The results show that the yield strength increases with decreasing finishing rolling temperature, whereas the tensile strength and total elongation exhibit relatively small variations. Significant changes in phase fraction, grain size, spatial distribution, and NbC precipitation behavior are observed under different finishing rolling temperatures. The microstructure mainly consists of polygonal ferrite and granular bainite, while acicular ferrite is formed at higher finishing rolling temperatures. With decreasing finishing rolling temperature, the ferrite and bainite grains are markedly refined and become more uniformly distributed. Meanwhile, the ferrite fraction slightly increases, the crystallographic texture is weakened, and, more importantly, the number density of precipitates increases while their size is significantly reduced. The hole expansion ratio increases noticeably with decreasing finishing rolling temperature, which is mainly attributed to grain refinement, improved microstructural and strain homogeneity, and the selective strengthening effect of fine NbC precipitates. These factors effectively reduce stress concentration and hardness mismatch between soft and hard phases, thereby delaying crack initiation during hole expansion.
Wu et al. (Wed,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: