The precursor infiltration and pyrolysis (PIP) route is widely adopted to fabricate carbon fiber-reinforced silicon carbide (Cf/SiC) composites; however, the atomic-scale restructuring of the pyrolytic carbon/silicon carbide (PyC/SiC) interface during ceramization—and its impact on mechanical integrity—remains elusive. Here, reactive molecular dynamics (ReaxFF MD) simulations elucidate the coupled thermochemical–mechanical evolution of polycarbosilane (PCS) precursors on PyC substrates with orientation angles (OAs) of 0°, 25°, 55°, and 85°. Dynamic pyrolysis triggers a pivotal transition from sp2 to sp3 hybridization at the interface. High-OA substrates (55° and 85°) present a dense population of reactive edge sites, fostering extensive cross-interfacial covalent bonding. Subsequent shear loading reveals that these pyrolysis-induced chemical bridges govern failure modes, shifting from interlayer sliding dominated by weak non-bonded interactions (0°) to ductile fracture featuring uniform plasticity and crack deflection. The OA = 55° interface attains a theoretical peak shear strength of 15 GPa and exhibits the most favorable combination of high strength and ductile failure under tensile loading, owing to an optimal balance between reactive site availability and interlayer steric openness. In contrast, the OA = 85° interface, despite comparable peak stress, fails via brittle crack penetration into the SiC matrix. By correlating atomistic structure with macroscopic performance, this study provides a bottom-up framework for engineering Cf/SiC composites via interfacial texturing and optimized pyrolysis protocols.
Zhang et al. (Fri,) studied this question.