Atomic layer deposition (ALD) is widely used to deposit conformal thin films but is often limited in the tunability of the resulting material’s properties. Substrate bias and electric fields alter precursor-surface interactions and provide means to tune material properties. To explore this, we performed zinc oxide (ZnO) ALD using diethylzinc (DEZ) and water on silicon native oxide substrates at 150 °C in a sample holder designed to create a static electrical field by biasing one plate of a parallel plate capacitor-style sample holder during deposition. ZnO films prepared in an electric field/on a biased sample holder were thinner, changed relative crystalline composition, and contained more carbon compared to samples grown in identical sample holders without bias. The thickness was independent of the magnitude of the eletric field between plates, indicating that the primary driver for the change was substrate biasing not the electric field between plates of the parallel plate capacitor-style sample holder. Density functional theory calculations showed enhanced electron migration between dissociatively adsorbed DEZ molecules and the ZnO (002) facet with increasing force from an electric field at the substrate surface, which strengthens the electronic interactions between the surface and the adsorbate. These models offer a compelling explanation for the inhibited growth, changes in the crystallinity, and increase in carbon content of films grown in an electric field/on biased plates.
Jones et al. (Fri,) studied this question.