Biochars are currently proposed as soil amendments or sorbent materials. There is an extensive scientific literature that deals with biochars originating from different raw materials. However, a holistic physicochemical characterization with simple analytical techniques is needed to provide insights on the characteristics of the biochars produced from malt spent rootlets (MSRs) and how they vary using different pyrolysis temperatures. This way, their properties can be fully understood, and they can be used for commercial purposes more effectively. Initially, the texture of the biochars were visualized by SEM and was quantified by the adsorption/desorption of nitrogen and the Brunauer, Emmett, and Teller (BET) equation. Additionally, the moisture content, the ash content and the pH of each sample were measured. Furthermore, the electrical conductivity of each sample was measured. Different techniques were used to determine the properties of carbon and of the surface functional groups (Total Carbon, XRD, ATR-FTIR) and leachable organic matter. Also, sorption of the methylene blue dye solution has been studied, which is an indication of mesopores for each biochar. Molasses number was also determined, as this is an indicator of macropores. Finally, the chlorine removal rate was determined for each type of biochar. The experiments marked that the change in mass of biochars has stopped after three hours at 50 °C in the drying oven. The measured moisture content ranged from 6 to 11%. The specific surface area of our materials, calculated through the BET equation, for low temperature biochars (e.g., 28 m2/g, at 350 °C), is much lower than that of high temperature pyrolyzed biochar (e.g., 286 m2/g, at 850 °C). The pH value ranged from 7 to 10. The electrical conductivity values of samples ranged from 800 μS/cm to 2.55 mS/cm, and these decreased during the measurement after the second wash with deionized water. Crystallinity increased with increasing pyrolysis temperature whereas the number of functional groups decreased. MSR biochars produced at temperatures equal or higher than 750 °C demonstrate different characteristics to the ones produced at lower temperatures.
Tzachristas et al. (Sat,) studied this question.