In the phenomenon regarding the electroluminescence, EL, in KI single crystals containing potassium metal colloids it is essential to clarify the characteristic roles of the hole type centers as well as electron trapped type centers in specimens. By making use of the specimens containing various centers, such as F-, F₂-center and potassium metal colloids the EL spectra were examined in detail at about 80K. It was found that there existed three EL luminescence peaks, e. g. , 240, 360, and 540nm. On the basis of the optical absorption measurements before and after EL measurements the change in the defect spectra in specimens was investigated on the three EL peaks. A proposal model was made as to the characteristic three EL peaks. The peak observed at 240nm was attributed to the interaction between the free electrons produced from the surface of the potassium metal colloids and F-centers in the course of EL process. Another 360 and 540nm peaks were considered to be related to the interaction among the F-aggregated centers and the hole type ceters produed from the potassium metal colloids. Brief discussion is given concerning the characteristic behavior of the potassium metal colloids in the process of the EL. |カリウム・コロイドを含むKI単結晶における電界発光現象の機構について知見を得るために, これまでにカリウム・コロイドの導入法の確立とその評価・同定法に関連する実験研究の成果の一部について報告を行ってきた。本研究では電界発光現象におけるカリウム・コロイド役割を明らかにする目的で付加着色法によって高濃度にF中心を導入できる条件下で, 急冷法ではなく炉中冷却の方法を採用し, カリウム・コロイド, F中心およびF₂中心を含むKI単結晶を試料として実験を行った。その結果, 約80Kの低温で電界発光のスペクトルを観測することにより, 240nm, 360nm, 540nmに発光ピークが存在することが明らかになった。電界発光測定前後の試料についての光学吸収スペクトルを基礎としてカリウム・コロイドと関連する種々の色中心のエネルギー準位を考慮してこれらの三つの発光ピークについてモデルを検討した。240nmのピークについては, 強電界下でカリウム・コロイド粒子から放出された電子が伝導帯に励起されて, 自由電子となり試料中を動きまわりF中心と会合してF^-中心を形成する際の放射光であるとした。さらに, 360nmと, 540nmとの発光ピークは, それぞれカリウム・コロイド粒子から放出された正孔型中心であるVₖ中心がF₂^+中心と会合する場合とVₖ中心から変換されたH中心がF中心と会合する場合の放射光であるとした。
萩原 et al. (Thu,) studied this question.