Molten salt electrodeposition is a promising technique to prepare high-performance tungsten coatings for fusion reactor first-wall components. However, the ultra-high temperature during deposition causes severe grain coarsening and precipitate dissolution in CuCrZr alloy substrates, resulting in dramatic mechanical property degradation. In this study, a thermal cycle at 1223.15 K for 100 h was employed to simulate the thermal impact of molten salt tungsten electrodeposition (MSE) on CuCrZr alloys, and an aging treatment (703.15 K for 12 h) was adopted to restore the degraded mechanical properties. After aging, the tensile strength and yield strength recovered to 378.35 ± 7.40 MPa and 261.02 ± 3.40 MPa, meeting the minimum tensile property requirements of ITER for CuCrZr alloys. The recovery is attributed to nano-sized Cr-rich phase precipitation and high-density dislocations, providing effective Orowan precipitation strengthening. This work provides the first simple, engineering-friendly post-treatment to repair performance degradation of CuCrZr under the extreme thermal exposure of molten salt electrodeposition, which is critical for large-scale fabrication of high-performance plasma-facing components (PFCs) for fusion reactors.
Dong et al. (Thu,) studied this question.