Sustainable and Green Surface Modification of Commercial Anatase TiO2 Using Licorice Root Waste Extract: Hydrothermal Processing and Calcination Effects on Structural Evolution

This study investigates the hydrothermal modification of commercial titanium dioxide (TiO2) in the presence of a natural licorice root extract (Glycyrrhiza glabra L.), serving as a stabilizing and growth-modulating agent. The experimental framework combines hydrothermal treatment in a Teflon-lined autoclave with subsequent thermal calcination to elucidate the structural, morphological, and chemical evolution of the material. The plant-based extract significantly influences particle assembly during synthesis, fostering the formation of an initial organic–inorganic hybrid system that results in enhanced morphological homogeneity compared to pristine TiO2. Thermal analyses (TGA and DSC) demonstrated the progressive decomposition of the organic components with increasing temperature, yielding a thermally stable, predominantly inorganic material at 600 °C. Scanning Electron Microscopy (SEM) observations confirmed a more uniform particle distribution in the modified samples. X-ray diffraction (XRD) patterns corroborated that the primary crystalline phase of TiO2 remains intact across all conditions, with structural variations limited to peak definition and long-range organization. Furthermore, FTIR spectroscopy supported the preservation of characteristic TiO2 vibrational features while indicating a gradual depletion of weakly bound surface species following thermal treatment. In conclusion, these findings demonstrate that natural extracts can effectively function as growth-modulating agents, steering material organization without altering its intrinsic chemical properties. This approach aligns with the principles of Green Chemistry and the circular economy, highlighting the potential of renewable plant-based resources as functional additives for the sustainable processing of inorganic materials. Rather than seeking to outperform commercial benchmarks, this work establishes a viable and low-environmental-impact strategy for morphological and structural modulation.