Elastic, dielectric, and piezoelectric constant matrix elements of a “single crystalline’’ (SC) film of vinylidene fluoride trifluoroethylene copolymer, P(VDF/TrFE), in which the orthorhombic 001 and 110 axes of fully extended chain crystals are preferentially oriented parallel to the stretching axis and normal to the surface, respectively, were measured at temperatures ranging from 10 K to the Curie point (402–404 K) by using a piezoelectric resonance method. All of the electromechanical coupling factors (k31, k32, k33, k24, and k15) are larger than those of conventional lamellar crystalline films. Some of the matrix elements for a P(VDF/TrFE) single crystal are derived from the measured values of constant matrix elements for the SC film. Some features characteristic of the SC film are revealed. The SC film has a large Young’s modulus for the stretching direction (1/s11) (121 GPa at 10 K). The properties related to the molecular motions along the chain axis, such as 1/s11, shear stiffness constant c55, shear piezoelectric constant e15, etc., exhibit strong relaxations around 250 K. The origin of these relaxations in the crystalline phase is discussed.
Omote et al. (Sat,) studied this question.