Thermal barrier coatings (TBCs) are effective protective and insulative coatings on hot section components of turbine engines. The quality and subsequent performance of the TBCs are strongly dependent on the adhesion between the coating and the metal substrate. The adhesion strength of TBCs varies depending on the substrate materials and coating, the coating technique used, the coating application parameters, the substrate surface treatments, and environmental conditions. Therefore, the roughness of the substrate surface has a significant effect on the performance of the TBC system. In this work, the roughness and microstructure of the 7YSZ (7 wt.% yttria-stabilised zirconia) top coat under different bond coat roughness treatments were studied. The purpose of this paper was to investigate the influence of the roughness of the bond coat on the adhesion of 7YSZ TBCs prepared by the electron beam–physical vapour deposition (EB-PVD) process. The VPA (vapour phase aluminium) bond coat was deposited on Inconel 718 nickel superalloy substrate using the above-the-pack technique. The ceramic top coat was applied to the bond coat using the EB-PVD process. The dependence between the TBC coating roughness and the bond coat roughness was determined. Adhesion strength measurements were performed according to the ASTM C 633 standard test method. The highest adhesion value observed in the tensile adhesion tests was 105 MPa. However, it was not determined whether the surface roughness of the bond coat affects the adhesion of the 7YSZ top coat.
Maciaszek et al. (Thu,) studied this question.