The mechanical and microstructural responses of ordinary Portland cement (OPC) and one-part geopolymer concrete (OPGC) to fibre reinforcement have not been scientifically explored, hence generating a research gap. As more construction industries seek high-performance and ecologically friendly building materials, geopolymer concrete is becoming more popular as an alternative to OPC. Because it does not need liquid activators, a one-part geopolymer system is advantageous, and adding fibres increases its tensile and flexural strength. Despite these benefits, a comprehensive evaluation of its strength performance in comparison to conventional OPC concretes requires more research. Four concrete mixes, which are ordinary Portland cement (OPC), fibre-reinforced ordinary Portland cement (FROPC), one-part geopolymer concrete (OPGC), and fibre-reinforced one-part geopolymer concrete (FROPGC), are examined in this study for their fresh, mechanical, and microstructural characteristics. Workability was assessed using slump tests, and at 7, 14, and 28 days, compressive, flexural, and split tensile strengths were measured. Stiffness, permeability, and internal quality were evaluated using the modulus of elasticity, water absorption, and ultrasonic pulse velocity (UPV), and microstructural examination was conducted using scanning electron microscopy (SEM). According to the findings, geopolymer concretes had better fresh qualities than OPC, with slump that were 20–31% higher. While fibre insertion greatly increased tensile and flexural strengths, it decreased workability. The highest compressive strength (63.78 MPa) was obtained by OPGC, whereas the highest flexural (15.1 MPa) and tensile (9.15 MPa) strengths were attained by FROPGC. Additionally, FROPGC showed the highest modulus of elasticity (44,040 N/mm 2 ), and a refined microstructure with fewer vacancies and well-bonded fibres was shown in FROPC and FROPGC. • We treated the three selected natural fibres with an alkaline solution to remove dirt and lignin. We carried out SEM analysis on both treated and untreated natural fibres. The morphologies show a rough and smooth surface for treated and untreated fibres, respectively. Also, all the treated fibres had a clean surface. The volumes of fibres used were 0%, 0.75%, and 1% at length of 25 mm. • We designed the constituents of natural fibre-reinforced one-part geopolymer concrete using the innovative Design of Experiment (DOE) method of conventional concrete design. This method, chosen due to the lack of a standard design method, offers a fresh perspective and unique approach to our research. Our target was 40 MPa after 28 days of curing. • We tested the samples of the prepared natural fibre-reinforced one-part geopolymer concrete for compressive, flexural, and split tensile strengths, impact resistance, MOE, Poisson ratio, UPV, and density. We carried out SEM analysis on natural fibre-reinforced one-part geopolymer concrete samples. • We developed models that show the relationship between the engineering properties of natural fibre-reinforced one-part geopolymer concrete. • Adding natural fibre to one-part geopolymer concrete samples improves flexural strength, split tensile strength, impact resistance strength, and MOE.
Ayeni et al. (Thu,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: