Hybrid MTMS–silica aerogels incorporating calcium silicate hydrate (C–S–H), the primary hydration product in cementitious systems, were synthesized via sol–gel processing followed by freeze-drying. The influence of C–S–H loading on pore structure, density, wettability, and thermal transport was investigated. The lowest thermal conductivity (0.068 W/m·K) and tap density (0.30 g/cm3) were obtained at 10% C–S–H loading (wM-CSH10), while the thermal conductivity increases to approximately 0.075–0.082 W/m·K at higher C–S–H content. All samples exhibit mesoporous structures with pore diameters in the range of 10–21 nm. Increasing C–S–H content progressively densified the network, reduced mesopore volume, and enhanced high-temperature mass retention up to 540 °C. FTIR analysis confirmed Si–O–Ca interfacial interactions, while nitrogen adsorption demonstrated persistent mesoporosity across all compositions. Thermal conductivity showed a positive correlation with density, indicating that bulk densification governs heat transport in the hybrid system. Beyond structural modification, the incorporation of C–S–H introduces chemical and microstructural features relevant to cement-based materials, suggesting potential compatibility with cementitious matrices. The results highlight the compositional trade-off between insulation efficiency and structural stability and demonstrate the potential of C–S–H-modified MTMS–silica aerogels for future integration into cement-based composites. These findings provide fundamental insight into their possible use in thermal insulation applications, such as building envelope systems (walls, façades, and roofs used for thermal insulation).
Kong et al. (Mon,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: