Accumulative roll bonding (ARB) is a severe plastic deformation process that enables the production of materials with ultrafine microstructures and enhances the characteristics of the base material, particularly in metal matrix composites. The primary objective of this study is to experimentally investigate the bonding strength in AA3105 strips that underwent the roll bonding process, with a specific focus on examining the influence of temperature and reduction rate on bonding. Three temperature levels (200 °C, 300 °C, and 400 °C) and three thickness reduction levels (35%, 50%, and 65%) were considered. The T-peel test was carried out to assess the bonding quality. It was employed to determine the peak force required to separate the two bonded strips. Additionally, ANOVA analysis was performed to develop a regression equation for analyzing peak force. Optical microscopy was used to evaluate the interface bonding quality in the longitudinal section. The results indicate that the bonding strength increases with both temperature and percentage reduction.
Carta et al. (2024) studied this question.