The molecular structures within the interfaces of the bulk heterojunction material comprising regioregular-poly(3-hexylthiophene-2,5-diyl), rrP3HT, and C(60) or its soluble derivative, 6,6-phenyl-C(61)butyric acid methyl ester, PCBM, have been studied by one- and two-dimensional nuclear magnetic resonance (NMR). The local structure within the interface was inferred from chemical shift (CS) data obtained from composite films (CFs) fabricated at room temperature (PCBMCF-RT and C(60)CF-RT) and from CFs that had been subsequently annealed at 150 degrees C for 30 min (PCBMCF-A150 and C(60)CF-150A). In PCBMCF-RT, the alkyl side chains of rrP3HT are close to the C(60) ball; C(60) is essentially 'wrapped' by the alkyl side chains. In PCBMCF-A150, the alkyl side chains self-assemble such that rrP3HT and PCBM are separated. The observation of well-defined splittings in the CS spectrum of the (13)C of C(60) in C(60)CF-A150 indicates a distortion from spherical symmetry. Measurements of the spin-lattice relaxation rate, 1/T(1), of C(60) imply local magnetic field fluctuations that arise from the dynamics of the C(60) distortion.
Yang et al. (2006) studied this question.