Characterization of Steel Industry Byproducts as Precursors in Alkali-Activated Binders

The civil construction and infrastructure sectors are known for their high environmental impact. Most of this impact is related to the carbon dioxide (CO2) emissions from Portland cement. As a sustainable alternative, alkali-activated binders (AABs) are explored for their potential to replace traditional binders. This research focused on AAB formulations using steel industry byproducts, such as Baosteel’s slag short flow (BSSF), coke oven ash (CA), blast furnace sludge (BFS), and centrifuge sludge (CS), as well as fly ash (FA) from a thermoelectric plant. Byproducts were characterized through laser granulometry, Fourier transform infrared spectroscopy (FTIR), X-ray fluorescence (XRF), X-ray diffraction (XRD), and scanning electron microscopy (SEM), followed by the formulation of AABs with different precursor ratios. After 28 days, the compressive strength was obtained for each formulation. Based on the compressive strength tests, two binary mixtures were selected for microstructural and chemical analyses through XRF, FTIR, and SEM. CA demonstrated the greatest potential for use in binary AABs based on BSSF, as it presented a higher source of aluminosilicates and smaller particle sizes. The formulations containing BSSF and CA achieved compressive strengths of up to 9.8 MPa, while the formulations with BSSF and FA reached 23.5 MPa. SEM images revealed a denser, more cohesive matrix in the FA-based AAB, whereas CA-based AABs showed incomplete precursor dissolution and higher porosity, which contributed to the lower mechanical strength of CA-based AABs. These findings highlight the critical role of precursor selection in developing sustainable AABs from industrial byproducts and demonstrate how different formulations can be tailored for specific applications.