The Effect of Support Layer Material and Adhesive Type on Compressive Dynamic Bending and Shear Strength in Laminated Wood

In this study, strength properties of wood material reinforced with carbon fiber fabric, steel wire mesh and bamboo veneer were determined. Polyvinylacetate (PVAc) and polyurethane (PUR) glues (D4)were used for the lamellas obtained from Scotch pine (Pinus sylvestris L.) and eastern beech (Fagus orientalis L.). Compressive strength according to TS EN 408+A1; dynamic bending (shock) strength according toTS ISO 13061-10 and shear strength according to ASTM D 3110 were determined on 3 and 5-layers samples. According to the results, the highest compressive strength (62.8 N/mm2) was found in 5-layerseastern beech samples reinforced with carbon fiber fabric and bonded with PUR glue. The highest dynamic bending strength value (110.8 kJ/m2) was found in 5-layerseastern beech samples reinforced with carbon fiber fabric and bonded with PUR glue and the highest shear strength value (12.3 N/mm2) in 3-layered eastern beech samples reinforced with steel wire mesh and bonded with PUR glue.