Structurally Regulated Design Strategy of Bi0.5Na0.5TiO3-Based Ceramics for High Energy-Storage Performance at a Low Electric Field

Dielectric ceramic capacitors are prospective energy-storage devices for pulsed-power systems owing to their ultrafast charge-discharge speed. However, low energy-storage density makes them difficult to commercialize for high-pulse-power technology applications. Herein, we presented a structurally regulated design strategy to disrupt a long-range ferroelectric order, refined grains, and eventually achieve excellent comprehensive energy-storage performance in (1 - x) (0.7Bi0.5Na0.5TiO3-0.3SrTiO3)-x Sm(Zn2/3Nb1/3)O3 eco-friendly ceramics. A large Wrec of ∼7.43 ± 0.05 J/cm3 and a high η of ∼85 ± 0.5% of 0.96 (0.7Bi0.5Na0.5TiO3-0.3SrTiO3)-0.04 Sm(Zn2/3Nb1/3)O3 were obtained at a low electric field of 290 kV cm-1 with good energy-storage temperature (25-120 °C), frequency (1-100 Hz) stability, and charge-discharge properties (PD ∼ 74 ± 1 MW/cm3 and τ0.9 ∼ 159 ± 2 ns). This strategy inspires rational structurally regulated designs and aims to promote the development of eco-friendly 0.7Bi0.5Na0.5TiO3-based ceramics with excellent energy-storage characteristics.