Influence of hydrogen sulphide on the corrosion and hydrogenation of 07Cr16Ni6 steel

The effect of hydrogen sulphide concentration on the corrosion behaviour of 07Cr16Ni6 austenitic-martensitic stainless steel in a 5% NaCl + 0.5% CH 3 COOH solution was studied to determine the role of H 2 S in the corrosion product formation and corrosion mechanism. Unstable passivation of steel is detected in a solution containing 100 mg/dm 3 H 2 S. When the pitting potential is reached, pitting damage occurs at the grain boundaries. The corrosion rate decreases by ∼five times after exposition for 720 h due to the formation of nickel and iron sulphides on the surface. Corrosion is accompanied by the absorption of 4.2–17.5 ppm hydrogen, 62…70% of which is diffusible and can cause hydrogen embrittlement. The scheme of steel corrosion under the influence of different concentrations of hydrogen sulphide is proposed.