Manipulating Stacking Fault Energy to Achieve Crack Inhibition and Superior Strength–Ductility Synergy in an Additively Manufactured High‐Entropy Alloy

Additive manufacturing (AM) is a revolutionary technology that heralds a new era in metal processing, yet the quality of AM-produced parts is inevitably compromised by cracking induced by severe residual stress. In this study, a novel approach is presented to inhibit cracks and enhance the mechanical performances of AM-produced alloys by manipulating stacking fault energy (SFE). A high-entropy alloy (HEA) based on an equimolar FeCoCrNi composition is selected as the prototype material due to the presence of microcracks during laser powder bed fusion (LPBF) AM process. Introducing a small amount (≈2.4 at%) of Al doping can effectively lower SFE and yield the formation of multiscale microstructures that efficiently dissipate thermal stress during LPBF processing. Distinct from the Al-free HEA containing visible microcracks, the Al-doped HEA (Al