Defect-Free Prussian Blue Analogue as Zero-Strain Cathode Material for High-Energy-Density Potassium-Ion Batteries

Prussian blue analogues (PBAs) have been widely studied as cathodes for potassium-ion batteries (PIBs) due to their three-dimensional framework structure and easily adjustable composition. However, the phase transition behavior and Fe(CN)64– anionic defects severely deteriorate electrochemical performances. Herein, we propose a defect-free potassium iron manganese hexacyanoferrate (K1.47Fe0.5Mn0.5Fe(CN)6·1.26H2O, KFMHCF-1/2) as the cathode material for PIBs. The Fe–Mn binary synergistic and defect-free effects can inhibit the cell volume change and octahedral slip during the K-ion insertion/extraction process, so that the phase transformation behavior (monoclinic ↔ cubic) is effectively inhibited, achieving a zero-strain solid solution mechanism employing Fe and Mn as dual active-sites. Thus, KFMHCF-1/2 contributes the highest initial capacity of 155.3 mAh·g–1 with an energy density of 599.5 Wh·kg–1 at 10 mA·g–1 among the reported PBA cathodes, superior rate capability, and cyclic stability over 450 cycles. The assembled K-ion full battery using K deposited on graphite (K@G) as anode also delivers high reversible specific capacity of 131.1 mAh·g–1 at 20 mA·g–1 and ultralong lifespans over 1000 cycles at 50 mA·g–1 with the lowest capacity decay rate of 0.044% per cycle. This work will promote the rapid application of high-energy-density PIBs.