Contribution of Nb addition to ductility and corrosion resistance of 06Cr13 stainless steel after dual-phase annealing and in-situ tensile study on deformation-fracture mechanisms
Puntos clave
Ductility and corrosion resistance improve significantly with Nb addition, enhancing performance under stress.
Key metrics show a 20% increase in ductility and a notable reduction in corrosion rates after processing.
Analysis of fracture mechanisms reveals that Nb addition influences deformation behavior during testing.
These findings suggest that optimizing Nb levels could significantly enhance the usability of stainless steel in various environments.