CoNi layered double hydroxides (CoNiLDHs) were successfully synthesized on nickel foam (NF) using a hydrothermal method. X-ray diffraction (XRD) analysis confirmed the formation of a well-defined hydrotalcite-like phase, including a strong (003) peak, indicating layered stacking. Scanning electron microscopy (SEM) revealed a 3D hierarchical nanosheet structure resembling flower-like arrays, which was further supported by EDS mapping showing a uniform distribution of Co, Ni, and O. Electrochemical studies demonstrated excellent OER activity, with a low overpotential of 188 mV at 10 mA/cm2 and a Tafel slope of 97.48 mV/dec, inferring rapid reaction kinetics. Furthermore, the material exhibited a significant electrochemical surface area (ECSA) compared to bare NF. Chronoamperometry over 24 h confirmed the operational durability catalyst, stabilizing around 7–8 mA/cm2, validating its potential as a cost-effective and efficient OER electrocatalyst in alkaline media.
BaQais et al. (Mon,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: