Measurement of InAsBi mole fraction and InBi lattice constant using Rutherford backscattering spectrometry and X-ray diffraction

Several 1 μm thick, nearly lattice-matched InAsBi layers grown on GaSb are examined using Rutherford backscattering spectrometry and X-ray diffraction. Random Rutherford backscattering measurements indicate that the average Bi mole fraction ranges from 0.0503 to 0.0645 for the sample set, and ion-channeling measurements indicate that the Bi atoms are substitutional. The X-ray diffraction measurements show a diffraction sideband near the main (004) diffraction peak, indicating that the Bi mole fraction is not laterally uniform in the layer. The average out-of-plane tetragonal distortion is determined by modeling the main and sideband diffraction peaks, from which the average unstrained lattice constant of each sample is determined. By comparing the Bi mole fraction measured by random Rutherford backscattering with the InAsBi lattice constant for the sample set, the lattice constant of zinc blende InBi is determined to be 6.6107 Å.