The segregation of brittle Laves phases remains a critical bottleneck limiting the performance of additive manufacturing (AM) nickel-based superalloys. While its evolution is governed by complex transient physical fields within the melt pool, a quantitative kinetic correlation between processing parameters and microstructural features is currently lacking. In this study, a high-fidelity multiphysics numerical model was developed to establish a cross-scale mapping logic of “Process-Physical Field-Microstructure” by dissecting the global distribution of temperature gradient (G) and solidification rate (R) along the quasi-steady-state melt pool boundary. It is revealed that increasing the scanning speed synergistically enhances R while compressing G. Beyond driving a transition from oriented columnar dendrites to refined mixed-dendritic structures, this shift effectively blocks the continuous enrichment channels of Nb and Mo elements by compressing the “kinetic time window” for solute redistribution. Consequently, the morphology of the Laves phase is forced to evolve from a continuous interconnected chain-like network into dispersed isolated particles. This research clarifies the kinetic essence of microstructural evolution under non-equilibrium solidification, providing critical physical criteria for the precise intervention of deleterious phases and the regulation of microstructural consistency in high-performance AM components.
Liu et al. (Mon,) studied this question.