Extended Interfacial Stability through Simple Acid Rinsing in a Li-Rich Oxide Cathode Material

deficiency and a partial reduction of Mn ions on the surface of the acid-treated material. More interestingly, although the irreversible oxygen evolution is greatly suppressed through the surface treatment, O K-edge resonant inelastic X-ray scattering shows that the lattice O-redox behavior is largely sustained. The acidic treatment, therefore, only optimizes the surface of the Li-rich material and almost eliminates the irreversible gas evolution, leading to improved cycling and rate performance. This work therefore presents a simple yet effective approach to passivate cathode surfaces against interfacial instabilities during high-voltage battery operation.