Microstructural Evolution of Hybrid Perovskites Promoted by Chlorine and its Impact on the Performance of Solar Cell

(Cl) perovskite films by using excess MACl-containing precursors, which exhibited approximately an order of magnitude larger grain size with higher -preferred orientation compared with that from stoichiometric precursors. Comprehensive mechanisms for the large grain evolution by Cl incorporation were elucidated in detail by correlating the changes in grain orientation, distribution of grain size, and the remaining Cl in the perovskite during thermal annealing. In the presence of Cl, - and -oriented grains grew faster than other grains at the initial stage of annealing. Further annealing led to the dissipation of Cl, resulting in the shrinkage of grains while grains continuously grew, as analyzed by x-ray rocking curve and diffraction. As a result of reduced grain boundaries and enhanced texture, the trap density of perovskite solar cells diminished by ~10% by incorporating MACl in the precursor, resulting in a fill factor more than 80%.