Helical Water Chain Mediated Proton Conductivity in Homochiral Metal–Organic Frameworks with Unprecedented Zeolitic unh-Topology

Four new homochiral metal-organic framework (MOF) isomers, Zn(l-L(Cl))(Cl)(H(2)O)(2) (1), Zn(l-L(Br))(Br)(H(2)O)(2) (2), Zn(d-L(Cl))(Cl)(H(2)O)(2) (3), and Zn(d-L(Br))(Br)(H(2)O)(2) (4) L = 3-methyl-2-(pyridin-4-ylmethylamino)butanoic acid, have been synthesized by using a derivative of L-/D-valine and Zn(CH(3)COO)(2)·2H(2)O. A three-periodic lattice with a parallel 1D helical channel was formed along the crystallographic c-axis. Molecular rearrangement results in an unprecedented zeolitic unh-topology in 1-4. In each case, two lattice water molecules (one H-bonded to halogen atoms) form a secondary helical continuous water chain inside the molecular helix. MOFs 1 and 2 shows different water adsorption properties and hence different water affinity. The arrangement of water molecules inside the channel was monitored by variable-temperature single-crystal X-ray diffraction, which indicated that MOF 1 has a higher water holding capacity than MOF 2. In MOF 1, water escapes at 80 °C, while in 2 the same happens at a much lower temperature (∼40 °C). All the MOFs reported here shows reversible crystallization by readily reabsorbing moisture. In MOFs 1 and 2, the frameworks are stable after solvent removal, which is confirmed by a single-crystal to single-crystal transformation. MOFs 1 and 3 show high proton conductivity of 4.45 × 10(-5) and 4.42 × 10(-5) S cm(-1), respectively, while 2 and 4 shows zero proton conductivity. The above result is attributed to the fact that MOF 1 has a higher water holding capacity than MOF 2.