This study describes a hydrometallurgical process to investigate the cerium recovery from rare earth polishing powder waste (REPPW) containing main elements such as cerium, lanthanum, praseodymium, neodymium, calcium and aluminum. First, dissolution experiments on La2O3, Pr2O3, Nd2O3, CaO and Al2O3 with 5 µm particle size in sulfuric acid solutions were carried out using a batch reactor with various acid concentrations (1–15 mol/dm3) at different temperatures (30–180°C). The effects of these two parameters on the dissolution reaction were studied. The obtained results showed that two sequential leaching steps were needed to separate cerium from the mixture of CeO2, La2O3, Pr2O3, Nd2O3, CaO and Al2O3. The total process for cerium recovery from REPPW via two-stage acid leaching was then developed through the collection of experimental results. Moreover, the dissolution rate of Al2O3 was expressed by a shrinking core kinetics model. The variation of the dissolution rate constant with temperature obeyed the Arrhenius equation with activation energy of 130 kJ·mol−1 and reaction rate constant as a function of the acid concentration of C0.41. On the basis of the above data, a k-T (reaction rate constant-reaction temperature) diagram for a CeO2–Al2O3–H2SO4–H2O system that permits rational extraction of CeO2 and Al2O3 was devised.
Um et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: