Preparation, characterization and thermal properties of the PS+Si based polymer nanocomposites

Polymer nanocomposites based on polystyrene and polycrystalline Si nanoparticles have been successfully synthesized using the solution-casting method. The scanning electron microscope and x-ray diffraction methods show that the Si nanoparticle size in the obtained nanocomposite was up to 50 nm. The thermostability of the obtained nanocomposite was studied depending on the concentration of Si nanoparticles in the PS matrix. It was found that Si nanoparticles that are distributed homogeneously in the polymer matrix act as a thermal barrier. By adding 3% Si nanoparticles into polystyrene polymer, the thermal degradation temperature of PS increases by 20°, and the decomposition rate reduces from −42,460 mg/min to −35,099 mg/min. In addition, it was shown that Si nanoparticles do not affect the PS glass transition temperature, which explains that the porous Si does not reduce the free volume for the polymer molecules to move. The polymer macromolecules just are adsorbed on the porous silicon surface, which partially limits their mobility.