This study examines how trace Al 2 O 3 additions (0.5 and 1.0 wt%) influence the microstructure, mechanical performance, and corrosion behavior of laser powder bed fused (LPBF) 316L stainless steel. Nano-alumina was mechanically mixed with 316L powder and processed by LPBF under two laser power conditions. Microstructural features were characterized using SEM, EBSD, TEM, and STEM-EDS. Mechanical properties were evaluated by room-temperature and elevated-temperature tensile testing, and corrosion behavior was assessed through potentiodynamic polarization and electrochemical impedance spectroscopy in 3.5 wt.% NaCl. Rather than remaining as inert ceramic particles, Al 2 O 3 undergoes partial dissolution and re-precipitation, forming nanoscale Al–Mn–Cr–O-rich features that are coherent with the austenitic matrix. These nanoscale oxide precipitates provide consistent strengthening through dislocation impediment, increasing yield strength at both Al 2 O 3 contents. A second population of microscale agglomerates is also observed and is associated with reduced ductility and localized corrosion susceptibility, particularly at 1.0 wt% Al 2 O 3 . Electrochemical testing shows that 0.5 wt% Al 2 O 3 improves pitting resistance, whereas higher additions reduce repassivation capability. A nominal addition of 0.5 wt% Al 2 O 3 yields the most favorable balance of strength, ductility, and corrosion resistance by maximizing beneficial nanoscale oxide precipitation while limiting detrimental microscale agglomeration.
Song et al. (Sun,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: