In the context of the “dual-carbon” targets and the development of green building materials, lightweight mortar has attracted considerable attention, owing to its low density and excellent thermal insulation properties. However, lightweight aggregates, such as vitrified microspheres, while effectively reducing mortar density, exhibit high porosity and weak interfacial bonding, which compromise mechanical performance. To address this issue, this study introduces sugarcane bagasse fiber (SBF) as a reinforcing material, with contents of 0%, 0.4%, 0.8%, 1.2%, and 1.6%. The effects of SBF on physical properties (consistency, density, water absorption) and mechanical properties (compressive strength, flexural strength, and tensile bond strength) were systematically evaluated. Furthermore, low-field nuclear magnetic resonance (LF-NMR) and scanning electron microscopy (SEM) were employed to analyze pore structure and interfacial transition zone (ITZ) characteristics at multiple scales. The results indicate that: (1) at low contents (0.4–0.8%), SBF was uniformly dispersed, improving matrix compactness; (2) compared with the control group, the 28-day compressive, flexural, and tensile bond strengths increased by 7.1%, 13.1%, and 25%, respectively; (3) NMR analysis revealed that the incorporation of SBF significantly increased the proportion of capillary pores, reduced total porosity, and enhanced mortar compactness, thereby improving mechanical strength; (4) fractal dimension analysis showed that contents of 0.4% and 0.8% increased structural complexity while reducing pore connectivity, leading to higher compressive strength; (5) SEM observations further demonstrated that the fibers provided bridging and anchoring effects within the ITZ, promoted the deposition of hydration products, and enhanced interfacial compactness.
Zhou et al. (Fri,) studied this question.