The study aimed to evaluate the effect of chlorhexidine (CHX), chlorin p6-mediated photodynamic therapy (PDT), magnesium oxide nanoparticles (MgONPs), and Clp6-functionalized MgONPs on smear layer removal and shear bond strength of a two-step etch-and-rinse adhesive to caries-affected dentin. Seventy-five human permanent molars with occlusal carious lesions and ICDAS scores of four and five were included. Twenty-five samples were used to prepare dentin discs 2 mm in thickness. The remaining samples, along with 25 discs, were arbitrarily allocated into five disinfectant groups, with n = 15 per group (10 teeth and 5 discs). Group I: Control, Group II: 2% CHX, Group III: Clp6-mediated PDT, Group IV: MgONPs, and Group V: Clp6-functionalized MgONPs. SL removal assessment, nanoparticle characterization, and EDX were performed using SEM. Fifty CAD were etched, followed by fifth-generation adhesive application and composite build-up. SBS and failure modes were evaluated with a universal testing machine and stereomicroscope, respectively. Group 4 (MgONPs) specimens displayed the maximum cleaning of SL (1.11 ± 0.13) and the highest SBS (10.32 ± 0.18 MPa). However, minimum SL removal (2.87 ± 0.94) and bond strength (7.42 ± 0.25 MPa) were exhibited by Group 1 (No disinfectant) samples. MgONPs possess the potential to be used as a cavity disinfectant, as they efficiently remove SL from CAD and augment the bond integrity outcomes.
AlRefeai et al. (Fri,) studied this question.