Additive manufacturing through a laser cladding has been shown to be an effective technology for the mitigation of wear and rolling contact fatigue (RCF) of railway track. Small-scale tests have consistently shown that creating a thin layer of premium material on the tribo-active surface of the railhead vastly reduces wear and suppresses the onset of RCF due to the ratcheting mechanism being almost eliminated in comparison to standard rail material. Cladding reduces material plastic flow by 60% which is a cause of insulated track joint failure. This paper reports results from the first full-scale trials of additively manufactured laser clad layers on railway rails by studying their mechanical properties and microstructure. This is a vital step in safely progressing this technology from lab scale to network application. Tested full-scale insulated block joint (IBJ) specimens, clad with martensitic stainless steel (MSS) and Stellite 6, were sectioned, polished and etched and the microstructures of the clad, heat-affected zone and parent rail materials were inspected using optical and scanning electron microscopy (SEM) (Hitachi TM3030 plus, Tokyo, Japan). Residual stress was also measured. Cladding with MSS and Stellite 6 showed high wear and RCF resistance after the tests. Material flow was reduced with the clad layer applied. No defects such as porosity or large precipitates were observed in the heat-affected zone (HAZ), particularly close to the rail surface at the clad end which could act as a point of weakness. Residual stress states varied between materials, MSS being compressive (−344 MPa average) and Stellite 6 being tensile (+391 MPa average) which could have an impact on the fatigue life of the clad. This finding matches previous work, indicating that MSS may be preferable in the field, where bending of rails can occur. Overall, the work showed that laser cladding can provide a good solution to lipping issues and wear problems of rail in IBJs. Analysis in this work confirmed that the HAZ where clad meets the bulk rail at the surface has good structural integrity; however, this needs to be a focus of attention in field application of these layers.
Lewis et al. (Fri,) studied this question.