Titanium compounds are an integral component for paint pigments, food additives (E171), catalysts, precursors for resistant structural materials, medicine, and water, and air purification and disinfection processes. A new and rather promising trend for titanium dioxide production is obtaining it from minerals with magnesium titanium structure. Magnesium titanates obtained by pyrometallurgical processing of quartz–leucoxene concentrate (oil sandstones). It was found that the optimal pyrometallurgical processing conditions were 4 h and a temperature of 1425–1450 °C, with TiO2 → MgXTiYOZ conversion exceeding 95%, and that sulfation of the magnesium titanate mixture with 60–70% H2SO4 for 150–210 min allows a 95% extraction of titanium compounds into solution. Investigation of the mechanism of titanium compound precipitation from Mg-Ti-containing sulfuric acid solutions revealed that in the pH range from 3 to 6, only titanium compounds were extracted from solution, while coprecipitation of magnesium compounds begins only at pH above 6.5. The product obtained by precipitation is titanium dioxide with an anatase structure, with particle distribution ranging from 0.8 to 5.0 µm and a developed surface area over 250 m2/g with mesopores characteristic of sorption materials.
Евгений Николаевич Кузин (2026) studied this question.