Enhancing wear and corrosion resistance of micro-arc oxidation coating on Mg-Gd-Zn-Zr alloy via TiO2 particles reinforcement
Key Points
Improved corrosion resistance in the alloy was observed with the application of TiO2 particles, enhancing its durability greatly.
The enhancement in wear resistance reaches up to 30% when reinforced with a specific concentration of TiO2 particles, which is notable.
Observational analysis involved testing the micro-arc oxidation coating on Mg-Gd-Zn-Zr alloy with varied TiO2 concentrations for optimal results.
These findings highlight the potential for using TiO2 particles to strengthen coating performance in industrial applications; further real-world testing is recommended.