The incorporation of reclaimed asphalt pavement (RAP) in asphalt mixtures improves sustainability but significantly reduces the intrinsic self-healing capacity due to binder aging. This study aimed to quantify whether epoxy-coated rejuvenator microcapsules could restore and enhance the self-healing performance of RAP-containing recycled asphalt mixtures. Four mixture types (AC-10C, AC-13C, AC-16C, and SMA-13C) containing 20% RAP were evaluated using a fracture–healing–refracture bending test (Repair index, RC) and a splitting healing strength ratio (SHSR) test to determine the effects of healing time, temperature, and microcapsule dosage. RC increased rapidly during the first 8 h of healing and then approached stabilization, with the growth rate falling below 2%, indicating 8 h as the practical optimum healing duration. RC increased from 0 °C to 45 °C due to enhanced binder mobility and diffusion, and slightly decreased at 60 °C because temperature-induced softening reduced peak bending strength. The highest self-healing capacity was obtained at a microcapsule dosage of 4% (by RAP mass). Under the optimum healing condition (8 h and 45 °C), RC increased by 10.38%–13.50% and SHSR increased by 14.35%–25.27% compared with mixtures without microcapsules. Among the mixtures, SMA-13C exhibited the highest self-healing capacity, followed by AC-13C, AC-10C, and AC-16C. The contribution of this study lies in quantifying the healing enhancement in RAP-containing mixtures, identifying practical optimum healing conditions based on a growth-rate criterion, and demonstrating consistent trends between two healing indices across different mixture structures.
Jia et al. (Sat,) studied this question.