To achieve the same service life of glass fiber reinforced polymer (GFRP) connectors and precast concrete sandwich panels, ensuring the structural stability and safety of the walls during long-term service, it is necessary to research the durability of GFRP connectors. In accordance with the ACI 440.3R-12 test method, an accelerated aging study was conducted by immersing 90 GFRP connectors in a simulated concrete pore solution at temperatures of 40 °C, 60 °C, and 80 °C for durations of 3.65, 18, 36.5, 92, and 183 days. This investigation aimed to analyze the effects of temperature and exposure time on the shear strength of the GFRP connectors. Scanning Electron Microscopy (SEM) was employed to analyze the micro-morphology of the specimens before and after exposure. The SEM observations revealed that after 183 days at 40 °C, the fiber-matrix interface remained relatively intact without significant debonding. However, at 60 °C, noticeable degradation occurred, characterized by corrosion of fibers and evident debonding from the surrounding matrix. At 80 °C, the GFRP specimens were severely damaged, precluding the extraction of viable samples for SEM analysis. The results further indicated that the most rapid decline in the shear strength occurred within the initial 3.65 days of exposure, with reductions of 8.62%, 10.12%, and 10.77% at 40 °C, 60 °C, and 80 °C, respectively. The degradation rate subsequently decelerated with prolonged exposure. After 183 days, the residual shear strength retention rates decreased by 21.03% and 26.89% at 40 °C and 60 °C, respectively. This behavior is primarily attributed to a high moisture absorption rate driven by a significant humidity gradient between the surface and the interior, leading to rapid swelling and plasticization of the vinyl ester resin matrix, which consequently reduced the stiffness and strength of the GFRP connectors. Finally, a predictive model for the time-dependent shear strength of GFRP connectors under various temperature conditions was developed based on Fick’s law.
Xue et al. (Sat,) studied this question.