Excellent Stability of a Lithium‐Ion‐Conducting Solid Electrolyte upon Reversible Li+/H+ Exchange in Aqueous Solutions

Batteries with an aqueous catholyte and a Li metal anode have attracted interest owing to their exceptional energy density and high charge/discharge rate. The long-term operation of such batteries requires that the solid electrolyte separator between the anode and aqueous solutions must be compatible with Li and stable over a wide pH range. Unfortunately, no such compound has yet been reported. In this study, an excellent stability in neutral and strongly basic solutions was observed when using the cubic Li7 La3 Zr2 O12 garnet as a Li-stable solid electrolyte. The material underwent a Li(+) /H(+) exchange in aqueous solutions. Nevertheless, its structure remained unchanged even under a high exchange rate of 63.6 %. When treated with a 2 M LiOH solution, the Li(+) /H(+) exchange was reversed without any structural change. These observations suggest that cubic Li7 La3 Zr2 O12 is a promising candidate for the separator in aqueous lithium batteries.