Solution‐Processable Glass LiI‐Li4SnS4 Superionic Conductors for All‐Solid‐State Li‐Ion Batteries

A new, highly conductive (4.1 × 10−4 S cm−1 at 30 °C), highly deformable, and dry-air-stable glass 0.4LiI-0.6Li4SnS4 is prepared using a homogeneous methanol solution. The solution process enables the wetting of any exposed surface of the active materials with highly conductive solidified electrolytes (0.4LiI-0.6Li4SnS4), resulting in considerable improvements in the electrochemical performance of these electrodes over conventional mixture electrodes. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.