Sulfate resistance of alkali-activated flyash-slag-lime concrete: comparative study of drying-wetting cycles and conventional exposure

Abstract Sulphate resistance of concrete is a crucial parameter for design of offshore structures. Of late alkali-activated materials are been given due consideration for infrastructure projects. In this context, the present study aims to assess the sulphate resistance of Alkali-Activated Concrete (AAC) with ternary blend of flyash-Ground Granulated Blast furnace Slag (GGBS) and limestone as the principal binder. The first phase of the study includes the optimization of ternary AAC mix with the inclusion of limestone as a potential binder to popularly used flyash slag blends. The inclusion of 5% limestone powder into the binder matrix is found to have beneficial effect on the mechanical properties of the ternary blended AAC. Further, an increase in the limestone powder content is not found to influence mechanical properties positively. The AAC mix with 5% limestone of total binder content was therefore selected for further evaluation of sulphate resistance. The sulfate resistance is evaluated under the alkaline media by subjecting AAC specimens to constant immersion and alternative drying and wetting cycles. The mechanical characteristics and mass reduction of the exposed samples were tested and compared with the conventional Ordinary Portland Cement (OPC) specimens. Evaluations were conducted over periods of 30, 45, 120, and 365 days of exposure. Scanning Electron Microscopy (SEM), and Energy Dispersion Spectroscopy (EDS) were also used to determine the surface morphology and mineral composition of samples after 365 days of exposure periods. The Flyash-Slag-Lime AAC exhibits denser morphology in comparison to OPC-based concrete, which in turn offers enhanced sulphate resistance.