Preparation and Properties of Lightweight Aggregates from Discarded Al2O3-ZrO2-C Refractories

Refractory materials are an important pillar for the stable development of the high-temperature industry. A large amount of waste refractories needs to be further disposed of every year, so it is of great significance to carry out research on the recycling of used refractories. In this work, lightweight composite aggregate was prepared by using discarded Al2O3-ZrO2-C refractories as the main raw material, and the performance of the prepared lightweight aggregate was improved by adjusting the calcination temperature and introducing light calcined magnesia additives. The results showed that the cold compressive strength and thermal shock resistance of the lightweight aggregates were significantly improved with increasing calcination temperature. Moreover, the introduction of light calcined magnesia can effectively improve the apparent porosity, cold compressive strength, and thermal shock resistance of the prepared lightweight aggregates at the calcination temperature of 1400 °C. Consequently, this work provides a useful reference for the resource utilization of used refractories, while the prepared lightweight aggregates are expected to be applied in the field of high-temperature insulation.