This study investigates the impact of cryogenic treatment duration on the mechanical properties and microstructural evolution of 6082 aluminum alloy subjected to subsequent artificial aging. Tensile tests were conducted using an electronic universal testing machine, and the microstructure was characterized by employing optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results indicate that both the tensile strength and elongation of the alloy first increase and then decrease with the extension of cryogenic treatment duration. The alloy treated with 12 h of cryogenic treatment followed by artificial aging at 180 °C for 8 h achieved a peak strength of 390 MPa. Meanwhile, the alloy treated with 8 h of cryogenic treatment and the same artificial aging process reached a maximum elongation of 13%. All specimens of 6082 aluminum alloy subjected to cryogenic and aging treatments exhibited ductile fracture under room temperature tensile conditions. The size of dimples at the fracture surface first increased and then decreased with increasing cryogenic treatment duration, indicating a transition from deeper to shallower dimples. The cryogenic treatment did not significantly affect the grain size of the alloy, which remained approximately 230 µm on average. Cryogenic treatment facilitated the precipitation of fine, densely distributed precipitates, enhancing the pinning effect of dislocations and thus improving the tensile strength. Additionally, cryogenic treatment increased the dislocation density and promoted the formation of subgrains, while the grain boundary precipitates transitioned from a continuous to a discontinuous distribution, all of which contribute to the enhancement of the plasticity.
Qiu et al. (Fri,) studied this question.