Different ageing treatments have been developed to achieve targeted properties in aluminum alloys through altering microstructures. However, there is a lack of understanding regarding the effect of ageing treatments on the formability of these alloys. In this study, we employed crystal plasticity finite element (CPFE) modeling, in conjunction with the Marciniak-Kuczynski (M-K) approach, to investigate the effects of ageing treatments on the mechanical properties and formability of AA6061 aluminum alloy. The as-received sheet was in the T6 heat treatment state, which was subjected to artificial ageing and pre-ageing, respectively, to achieve two age-hardened alloys with modified precipitation states. The microstructures and crystallographic textures of the three alloys were measured using the electron backscattering diffraction (EBSD) technique, and uniaxial tensile tests were performed along the rolling direction (RD), transverse direction (TD), and diagonal direction (DD, 45° to the RD) for each alloy. The forming limit curve (FLC) of the as-received alloy was determined using the Nakazima test. The dependence of mechanical strength, tensile ductility, and work-hardening behavior on the ageing treatments was clarified. Then, the tensile test results were utilized to calibrate the modeling parameters used in the CPFE model, whereas the FLC predictability of the developed model was validated with the experimental one. In the formability analysis, the effects of the ageing treatment on the FLC exhibit a notable dependency on loading paths, and the pre-aged alloy exhibits better formability than the other two at the plane strain tension state, thanks to its high work-hardening levels. In addition, the deformed textures along the different loading paths and the effects of the initial texture on the FLC are also discussed.
Wang et al. (Fri,) studied this question.