Alkali-activated materials can significantly reduce carbon dioxide emissions compared with cement. However, their durability remains insufficiently understood. This study investigated the effects of calcium hydroxide (Ca(OH)2, CH), an expansion agent (calcium sulfoaluminate, CSA), and a shrinkage-reducing agent (SRA) on the compressive strength and length change and determined the optimal content levels for each agent. Experiments were conducted to evaluate the compressive strength and length change of 17 mortar mixtures containing CH, CSA, and SRA. The substitution ratios of CH, CSA, and SRA were fixed at three predefined levels for each factor. The microstructural changes induced by the use of each agent were analyzed using pH measurements, porosity analysis, and X-ray diffraction. In addition, the water desorption behaviors associated with CSA and SRA were assessed. Experimental and statistical analyses demonstrated that the optimal contents of CH, CSA, and SRA for simultaneously improving the compressive strength and length change were 8.54, 10.0, and 0.76 wt.%, respectively. The use of CSA significantly enhanced the compressive strength development and dimensional stability of the mortar. This improvement was associated with a reduction in the porosity, which was attributed to ettringite formation. Furthermore, while the SRA slightly reduced the compressive strength, it significantly improved the dimensional stability.
Na et al. (Tue,) studied this question.